Olefin(base)Thermoplastic Elastomer

Item	Method	Unit	7023	7053	MC601	MC616	MC707	MC717
Density	JIS K7112	g/cm3	0.89	0.89	0.89	0.89	0.89	0.89
MFR (230, 21.2N)	JIS K7210	g/10min	2	7	3.2	21	3.3	2.7
Hardness Duro-A	JIS K6253	-	-	-	-	-	94	85
Flexural modulus	JIS K7203	MPa	320	310	500	600	85	-
Flexural strength		MPa	11	11	19	19	4	-
Tensile strength at yield	JIS K6251	MPa	13	13	19	20	7	-
Tensile strength at break			39	32	36	35	21	18
Tensile elongation at break		%	1090	990	920	940	880	1010
Izod impact strength	JIS K7110	KJ/m2	N.B. (-20)	7.5 (-20)	-	7 (23)	N.B. (-30)	N.B. (-30)
Haze (2mmt)	JIS K7136	%	42	69	52	56	33	13
Melting peak point	JIS K7121		165	165	127	134	162	160
Proper mold process	-	-	Extrusion	Injection / Extrusion	Injection / Extrusion	Injection	Extrusion	Extrusion
Japan pharmacopoeia (Container) Conformity	-	-	Conform	Conform	Conform	Conform	Conform	Conform
Sterilization	-	-	Autoclave	Autoclave	EB Radiation Autoclave	Autoclave	Autoclave	Autoclave

Values given here are taken in good faith at our laboratory and as a guide without warranty.